Bioactivity and properties of an adhesive system functionalized with an experimental niobium-based glass.

OBJECTIVE: This study evaluated the incorporation of niobophosphate bioactive glass (NbG) fillers into a commercial adhesive resin. MATERIALS AND METHODS: The silanized (NbGs) or non-silanized (NbG) NbG was added to the commercial adhesive system One Step (OS) at 30% by weight; unfilled adhesive served as control. The bioactivity of adhesives was analyzed by SEM and FTIR/ATR after 28 days in PBS. The adhesives were evaluated as regards microtensile bond strength immediately and after six months (n = 6); degree of conversion (n = 3), microhardness (n = 5); and radiopacity (n = 3). Data from each test were submitted to ANOVA and Tukey tests (P <0.05). RESULTS: FTIR/ATR analysis showed phosphate and carbonate precipitates on the NbG adhesive specimen surface. Statistical analysis of microtensile bond strength values showed that material x time interaction was not significant, but NbG group values were similar to those of unfilled adhesive (p <0.05). Addition of NbG did not alter the degree of conversion, but did increase microhardness and radiopacity values of the adhesive systems compared with those of the control group (OS). Incorporation of NbG into the adhesive system did not compromise the properties of the adhesive. CONCLUSION: A smart adhesive system with bioactive properties, high radiopacity, microhardness, and similar bond strength and degree of conversion was obtained by incorporating 30% by weight of NbG.

Adhesives Doped with Bioactive Niobophosphate Micro-Filler: Degree of Conversion and Microtensile Bond Strength.

To evaluate the effect of incorporating niobium phosphate bioactive glass (NbG) into commercial etch-and-rinse adhesive systems, with and without silane, on their degree of conversion (DC) (%) and microtensile bond strength (µTBS). The NbG micro-filler was added to two etch-and-rinse adhesive systems: One Step (OS) and Prime & Bond (PB) at 40% concentration. The following groups were formed: control without glass addition OS; addition of unsilanized NbG (OSNbG); addition of silanized NbG (OSNbGS); control without glass PB; addition of unsilanized NbG (PBNbG); addition of silanized NbG (PBNbGS). The DC was determined using total Fourier spectroscopy reflection (FTIR/ATR). For µTBS testing, 48 human third molars (n=8) were restored and sliced to obtain specimens (0.8 mm2) and they were tested at two different time intervals: immediately and after 6 months. The fracture mode was evaluated with a stereoscopic loupe (40×) and by scanning electron microscopy (SEM). The data were subjected to ANOVA and Tukey tests (a=0.05). NbG addition did not compromise the adhesive system DC values (p>0.05). Furthermore, the NbG added to the adhesive systems did not affect µTBS values (p>0.05). Fracture occurred predominantly at the dentin-adhesive interface. NbG bioactive glass did not affect the DC or microtensile bond strength results.

Adhesives Doped with Bioactive Niobophosphate Micro-Filler: Degree of Conversion and Microtensile Bond Strength

Abstract To evaluate the effect of incorporating niobium phosphate bioactive glass (NbG) into commercial etch-and-rinse adhesive systems, with and without silane, on their degree of conversion (DC) (%) and microtensile bond strength (μTBS). The NbG micro-filler was added to two etch-and-rinse adhesive systems: One Step (OS) and Prime & Bond (PB) at 40% concentration. The following groups were formed: control without glass addition OS; addition of unsilanized NbG (OSNbG); addition of silanized NbG (OSNbGS); control without glass PB; addition of unsilanized NbG (PBNbG); addition of silanized NbG (PBNbGS). The DC was determined using total Fourier spectroscopy reflection (FTIR/ATR). For μTBS testing, 48 human third molars (n=8) were restored and sliced to obtain specimens (0.8 mm2) and they were tested at two different time intervals: immediately and after 6 months. The fracture mode was evaluated with a stereoscopic loupe (40×) and by scanning electron microscopy (SEM). The data were subjected to ANOVA and Tukey tests (a=0.05). NbG addition did not compromise the adhesive system DC values (p>0.05). Furthermore, the NbG added to the adhesive systems did not affect μTBS values (p>0.05). Fracture occurred predominantly at the dentin-adhesive interface. NbG bioactive glass did not affect the DC or microtensile bond strength results.

Resumo Avaliar o efeito da incorporação de vidro niobofosfato bioativo (NbG, 40% em peso) em dois sistemas adesivos simplificados convencionais (One Step [OS] e Prime & Bond {PB}) com e sem silano, no grau de conversão (%) e resistência de união (RU) após 6 meses. Os seguintes grupos foram testados: Controle OS: sem adição de partículas; OS e adição de NbG sem silano (OSNbG); OS e adição de partículas silanizadas NbG (OSNbGS); Controle PB: sem adição de partículas; PB e adição de partículas de NbG sem silano (PBNbG); PB e adição de partículas silanizadas NbG (PBNbGS). O grau de conversão (GC) foi determinado utilizando espectroscopia de Fourier (FTIR/ATR). Para RU, 48 terceiros molares humanos (n=8) foram restaurados e cortados para obter corpos-de-prova (0,8 mm2) e, em seguida, testados em dois momentos: imediato e após seis meses. O padrão de fratura foi avaliado com lupa estereoscópica (40×) e microscópio eletrônico de varredura (MEV). Os dados foram submetidos à análise de variância e Tukey (a=0,05). NbG não comprometeu valores de GC dos sistemas adesivos (p>0,05). Além disso, a adição de NbG aos sistemas adesivos não afetou os valores de RU (p>0,05). O padrão de fratura ocorreu predominantemente na interface dentina-adesivo. NbG não afetou os resultados de GC e RU.

Comparative analysis of polymerization shrinkage of different resin composites.

This study sought to compare the shrinkage of 3 resin composites after polymerization, using different curing modes and 2 methods of analysis, with 45 samples in each group. To evaluate free linear shrinkage, specimens were prepared in Teflon molds (8 mm diameter x 2 mm thick) with 1 of 2 methacrylate-based resins or a silorane-based resin. To evaluate wall-to-wall shrinkage, cavities (1.5 mm thick x 3 mm diameter) were prepared in 45 healthy bovine incisors and then restored. In both tests, the same curing lights were used: conventional quartz-tungsten-halogen, a conventional light-emitting diode (LED), and an exponential LED. Gaps were measured microscopically, and the gap percentage was calculated. The results were analyzed by 2-way ANOVA and Tukey's test (α = 0.05). Curing modes differed significantly in the free linear shrinkage test group, while resin composites did not. In the wall-to-wall shrinkage group, there were significant differences between the resin composites.

Evaluation of pH, ultimate tensile strength, and micro-shear bond strength of two self-adhesive resin cements.

The aim of this study was to evaluate the pH, ultimate tensile strength (UTS), and micro-shear bond strength (µSBS) of two self-adhesive resin cements to enamel and dentin. Sound bovine incisors (n = 10) and two self-adhesive resin cements (i.e., RelyX U-100 and seT PP) were used. The pH of the resin cements was measured using a pH-indicator paper (n = 3). Specimens for UTS were obtained from an hourglass-shaped mold. For µSBS, cylinders with internal diameter of 0.75 mm and height of 0.5 mm were bonded to the flat enamel and dentin surfaces. Bonded cylinders were tested in the shear mode using a loop wire. The fracture mode was also evaluated. The cement seT PP showed a low pH; U-100 showed significantly higher UTS (49.9 ± 2.0) than seT PP (40.0 ± 2.1) (p < 0.05) and high µSBS to enamel (10.7 ± 3.7). The lowest µSBS was found for seT PP to dentin (0.7 ± 0.6); seT PP to enamel (4.8 ± 1.7), and for U-100 to dentin (7.2 ± 1.9), showing an intermediate µSBS value (p < 0.05). Adhesive failure was the most frequently observed failure mode. The resin cement that presented the lowest pH and UTS also presented the lowest micro-shear bond strength to enamel and dentin.

Low shrinkage composite resins: influence on sealing ability in unfavorable C-factor cavities.

The present investigation observed the sealing ability of low shrinkage composite resins in large and deep cavities, placed and photocured in one increment. Large, deep cavities (5.0 mm diameter and 2.5 mm deep) surrounded by enamel were prepared in bovine teeth, which were then divided into five groups. Groups 1, 2, 3 and 4: acid conditioning + Adper Single Bond (3M/ESPE, St Paul, MN, USA) and restoration with Aelite LS Posterior (BISCO Inc. Schaumburg, IL, USA) (G1); Filtek Z-350 (3M/ESPE,St Paul, MN, USA) (G2); Filtek Z-350 Flow (3M/ESPE, St Paul, MN, USA) (G3); Premisa (KERR Corporation, Orange, CA, USA) (G4). Group 5: Silorane Adhesive system (3M/ESPE, St Paul, MN, USA) + restoration with Filtek Low Shrinkage Posterior P90 (3M/ESPE, St Paul, MN, USA). After polymerization, the teeth were immersed in 0.5% basic fuchsine solution and immediately washed. Using the Imagetool Software, the extent of dye along the margins was calculated as a percentage of total perimeter. The restorations were then transversally sectioned and the depth of dye penetration was calculated in mm, using the same software. Kruskal-Wallis analysis for all groups showed no statistical differences for extent (p = 0.54) or depth (p = 0.8364) of dye penetration. According to this methodology, the so-called low shrinkage composite resins had the same sealing ability compared to regular and flowable nanocomposite materials.

Avaliação da sensibilidade pós-operatória em restaurações diretas profundas utilizando sistemas adesivos autocondicionantes / Evaluation of postoperative sensitivity in deep direct restorations using self-etching adhesive systems

O propósito de presente estudo foi avaliar a sensibilidade pós-operatória (SPO) após 2 dias, 7 dias, 180 dias e 360 dias, em restaurações de dentes posteriores feitas com resina composta (Z-350, 3M-ESPE) associada a adesivos autocondicionantes. Foram realizadas 60 restaurações em 35 pacientes e os grupos experimentais foram assim delineados: GI= 20 cavidades tratadas com o sistema adesivo de três passos SBMU (3M-ESPE); GII= 20 cavidades tratadas com o sistema autocondicionante de dois passos Adper SE Plus (3M_ESPE); GIII= 20 cavidades tratadas com o sistema autocondicionante de um passo All Bond SE (BISCO). Após 48 horas, 7 dias, 180 dias e 360 dias, os pacientes foram chamados para avaliação da SPO. Inicialmente, o relato do paciente era considerado e classificado de zero a três, de acordo com critérios previamente estabelecidos. Posteriormente, teste clínico com frio era realizado e classificado de zero a dez, de acordo com a escala visual analógica modificada. Os resultados foram analisados pelos testes não paramétricos de Kruskall-Wallis, para comparar os diferentes tratamentos ao longo do tempo; e teste de Friedman, para analisar o comportamento de cada sistema ao longo dos períodos. Os testes estatísticos não mostraram diferenças significativas de SPO para os grupos testados em todos os períodos avaliados. Os resultados mostraram que, nesse caso, a SPO não foi influenciada pelos sistemas autocondicionantes.

Low shrinkage composite resins: influence on sealing ability in unfavorable C-factor cavities

The present investigation observed the sealing ability of low shrinkage composite resins in large and deep cavities, placed and photocured in one increment. Large, deep cavities (5.0 mm diameter and 2.5 mm deep) surrounded by enamel were prepared in bovine teeth, which were then divided into five groups. Groups 1, 2, 3 and 4: acid conditioning + Adper Single Bond (3M/ESPE, St Paul, MN, USA) and restoration with Aelite LS Posterior (BISCO Inc. Schaumburg, IL, USA) (G1); Filtek Z-350 (3M/ESPE,St Paul, MN, USA) (G2); Filtek Z-350 Flow (3M/ESPE, St Paul, MN, USA) (G3); Premisa (KERR Corporation, Orange, CA, USA) (G4). Group 5: Silorane Adhesive system (3M/ESPE, St Paul, MN, USA) + restoration with Filtek Low Shrinkage Posterior P90 (3M/ESPE, St Paul, MN, USA). After polymerization, the teeth were immersed in 0.5 percent basic fuchsine solution and immediately washed. Using the Imagetool Software, the extent of dye along the margins was calculated as a percentage of total perimeter. The restorations were then transversally sectioned and the depth of dye penetration was calculated in mm, using the same software. Kruskal-Wallis analysis for all groups showed no statistical differences for extent (p = 0.54) or depth (p = 0.8364) of dye penetration. According to this methodology, the so-called low shrinkage composite resins had the same sealing ability compared to regular and flowable nanocomposite materials.

Sensibilidade pós-operatória em restaurações diretas extensas utilizando sistemas adesivos convencionais atuais / Postoperative sensitivity in large direct restorations using new total etch adhesive systems

O objetivo deste trabalho clínico foi avaliar a sensibilidade pós-operatória após 2, 7, 180 e 365 dias em restaurações de resina composta realizadas em cavidades amplas e profundas em dentes posteriores empregando-se três sistemas adesivos convencionais atuais (condicionamento ácido total+adesivo). Foram realizados 60 procedimentos restauradores pelo mesmo operador, divididos em três grupos com 20 amostras em cada: SB - ADPER SingleBond 2 (3M ESPE®); AB - All Bond 3 (Bisco®); e XP - XP Bond (Dentsply®). Todas as restaurações foram preenchidas com a resina Z350 (3M ESPE®) e os resultados foram submetidos aos testes de Kruskall Wallis e Friedman. Todos os resultados para sensibilidade pós-operatória foram semelhantes ao longo dos tempos testados.

Clinical evaluation of postoperative sensitivity using self-etching adhesives containing glutaraldehyde.

The present clinical study aimed to assess the postoperative sensitivity (POS) after 48 hours and seven days in occlusal restorations bonded with three different adhesive systems, two of them containing glutaraldehyde. The restorative procedures were performed using the three-step etch-and-rinse Adper SBMP-Plus adhesive (SBMP), the two-step etch-and-rinse Gluma Comfort One Bond + Desensitizer adhesive (GC+D) and the all-in-one self-etching/priming I Bond (IB) adhesive, which also has glutaraldehyde in its formula. All cavities were restored with Filtek Supreme nanoparticle composite resin. After 48 hours and seven days the patients were recalled and the postoperative sensitivity evaluated. The data analyzed by non-parametric Friedman test showed no significant differences in POS among the three tested groups after 48 hours and seven days.

Clinical evaluation of postoperative sensitivity using self-etching adhesives containing glutaraldehyde

The present clinical study aimed to assess the postoperative sensitivity (POS) after 48 hours and seven days in occlusal restorations bonded with three different adhesive systems, two of them containing glutaraldehyde. The restorative procedures were performed using the three-step etch-and-rinse Adper SBMP-Plus adhesive (SBMP), the two-step etch-and-rinse Gluma Comfort One Bond + Desensitizer adhesive (GC+D) and the all-in-one self-etching/priming I Bond (IB) adhesive, which also has glutaraldehyde in its formula. All cavities were restored with Filtek Supreme nanoparticle composite resin. After 48 hours and seven days the patients were recalled and the postoperative sensitivity evaluated. The data analyzed by non-parametric Friedman test showed no significant differences in POS among the three tested groups after 48 hours and seven days.

Cimentos autoadesivos: inter-relação dentina-cimento-pino / Self-adhesive luting cements: dentin-cement-post relationship

Os pinos pré-fabricados, cimentados nos condutos radiculares, são utilizados para aumentar a retenção do material de reconstrução e, em associação com a restauração indireta, aumentam a resistência do conjunto. O interior do conduto radicular é particularmente de difícil acesso e visualização. Assim, simplifica o protocolo de cimentação reduz a possibilidade de erros. Os cimentos autoadesivos, em virtude de sua fácil manipulação e aplicação, têm sido propostos para essa finalidade. No entanto, é necessário que a inter-relação desses materiais com a dentina e com o pino seja mais bem estudada e compreendida, bem como os aspectos relacionados à reação de polimerização. Sendo assim, este artigo tem como propósito apresentar informações das caracteristicas desse tipo de cimento, sua relação com a dentina e pino, com base em informações da literatura específica, bem como por meio de imagens obtidas com microscopia eletrônica de varredura (MEV).